Strontium aluminate

Strontium aluminate

Names
IUPAC name Dialuminum strontium oxygen(2-)
Identifiers
CAS Number	12004-37-4 Y
3D model (Jmol)	Interactive image
ECHA InfoCard	100.031.310
EC Number	234-455-3
PubChem	165931
InChI InChI=1S/2Al.5O.2Sr/q2*+3;5*-2;2*+2
SMILES [O-2].[O-2].[O-2].[O-2].[O-2].[Al+3].[Al+3].[Sr+2].[Sr+2]
Properties
Chemical formula	SrAl2O4
Molar mass	205.58 g/mol
Except where otherwise noted, data are given for materials in their standard state (at 25 °C [77 °F], 100 kPa).
Infobox references

Strontium aluminate (SRA, SrAl, SrAl₂O₄) is a solid odorless, nonflammable, pale yellow, monoclinic crystalline powder, heavier than water. It is chemically and biologically inert. When activated with a suitable dopant (e.g. europium, then it is labeled SrAl₂O₄:Eu), it acts as a photoluminescent phosphor with long persistence of phosphorescence.

There are also other strontium aluminates, e.g. SrAl₄O₇ (monoclinic), Sr₃Al₂O₆ (cubic), SrAl₁₂O₁₉ (hexagonal), Sr₄Al₁₄O₂₅ (orthorhombic).

Phosphor

For many phosphorescent-based purposes, strontium aluminate is a vastly superior phosphor to its predecessor, copper-activated zinc sulfide; it is about 10 times brighter and 10 times longer glowing, however it is about 10 times more expensive than ZnS:Cu and it cannot produce the unique red phosphorescence of the latter. It is frequently used in glow in the dark toys, where it displaces the cheaper but less efficient ZnS:Cu. However, the material has high hardness, causing abrasion to the machinery handling it; manufacturers frequently coat the particles with a suitable lubricant when adding them to a plastic.

Different aluminates can be used as the host matrix. This influences the wavelength of emission of the europium ion, by its covalent interaction with surrounding oxygens, and crystal field splitting of the 5d orbital energy levels.^[1]

Strontium aluminate phosphors produce green and aqua hues, where green gives the highest brightness and aqua the longest glow time. The excitation wavelengths for strontium aluminate range from 200 to 450 nm. The wavelength for its green formulation is 520 nm, its blue-green version emits at 505 nm, and the blue one emits at 490 nm. Colors with longer wavelengths can be obtained from the strontium aluminate as well, though for the price of some loss of brightness.

For europium-dysprosium doped aluminates, the peak emission wavelengths are 520 nm for SrAl₂O₄, 480 nm for SrAl₄O₇, and 400 nm for SrAl₁₂O₁₉.^[2]

SrAl₂O₄:Eu²⁺,Dy³⁺ is important as a persistently luminiscent phosphor for industrial applications. It can be produced by molten salt assisted process at 900 °C.^[3]

The most described kind is the stoichiometric green-emitting (approx. 530 nm) SrAl₂O₄:Eu²⁺. SrAl₂O₄:Eu²⁺,Dy³⁺,B³⁺ shows significantly longer afterglow than the europium-only doped material. The Eu²⁺ dopant shows high afterglow, while Eu³⁺ has almost none. Polycrystalline SrAl₁₂O₁₉:Mn is used as a green phosphor for plasma displays, and when doped with praseodymium or neodymium it can act as a good active laser medium. Sr_0.95Ce_0.05Mg_0.05Al_11.95O₁₉ is a phosphor emitting at 305 nm, with quantum efficiency of 70%. Several strontium aluminates can be prepared by the sol-gel process.^[4]

The wavelengths produced depend on the internal crystal structure of the material. Slight modifications in the manufacturing process (the type of reducing atmosphere, small variations of stoichiometry of the reagents, addition of carbon or rare-earth halides) can significantly influence the emission wavelengths.

Strontium aluminate phosphor is usually fired at about 1250 °C, though higher temperatures are possible. Subsequent exposure to temperatures above 1090 °C is likely to cause loss of its phosphorescent properties. At higher firing temperatures, the Sr₃Al₂O₆ undergoes transformation to SrAl₂O₄.^[5]

The glow intensity depends on the particle size; generally, the bigger the particles, the better the glow.

Strontium aluminate based afterglow pigments are marketed under brand names like Art 'N Glow, Core Glow,^[6] Ambient Glow Technology or AGT.^[7] Super-LumiNova ^[8][9] or NoctiLumina.^[10]

Strontium aluminate doped with europium and dysprosium is called Lumibrite developed by Seiko and claimed to be brighter and longer glow time compare to ordinary strontium aluminate doped with only europium.

Europium-doped strontium aluminate nanoparticles are proposed as indicators of stress and cracks in materials, as they emit light when subjected to mechanical stress (mechanoluminescence). They are also useful for fabricating mechano-optical nanodevices. Non-agglomerated particles are needed for this purpose; they are difficult to prepare conventionally but can be made by ultrasonic spray pyrolysis of a mixture of strontium acetylacetonate, aluminium acetylacetonate and europium acetylacetonate in reducing atmosphere (argon with 5% of hydrogen).^[11]

Cerium and manganese doped strontium aluminate (SrAl₁₂O₁₉:Ce,Mn) shows intense narrowband (22 nm wide) phosphorescence at 515 nm when excited by ultraviolet radiation (253.7 nm mercury emission line, to lesser degree 365 nm). It can be used as a phosphor in fluorescent lamps for e.g. photocopiers. A small amount of silicon substituting the aluminium can increase emission intensity by about 5%; the preferred composition of the phosphor is SrAl₁₁Si_0.75O₁₉:Ce_0.15Mn_0.15.^[12]

Structural material

Strontium aluminate cement (SrAl₂O₄, or SrO.Al₂O₃) can be used as refractory structural material. It can be prepared by sintering of a blend of strontium oxide or strontium carbonate with alumina, in a roughly equimolar ratio, at about 1500 °C. It can be used as a cement for refractory concrete for temperatures up to 2000 °C. Barium aluminate cement has similar characteristics, and can be furthermore used as radiation shielding. The use of barium and especially strontium aluminate cements is limited by the availability of the raw materials.^[13]

Strontium aluminates are examined as proposed materials for immobilization of fission products of radioactive waste, namely the strontium-90.^[14]

References

External links

• How does glow-in-the-dark stuff work?
• Facts, pictures, stories about the element Strontium
• Performance Demonstrations of Zinc Sulfide and Strontium Aluminate Photoluminescent Floor Proximity Escape Path Marking Systems